Clear Float Solar Glass
Thickness: 2.8mm, 3.2mm, 4.0mm
Applications:Cover glass for solar thermal collector
Glass backsheet for glass-glass photovoltaic modules
Greenhouse roof and wall
GLASS DESCRIPTION
●MIGO Clear Float Solar Glass is produced by processing high quality clear float glass in continuous tempering furnace. After tempering treatment, it is 4-5 times stronger than ordinary annealed float glass and, if broken, disintegrates into small fragments with dulled edges that are unlikely to cause serious injury.
●Light transmittance is a bit lower than ultra clear low iron glass, but cost is also lower. It is suitable for area having sufficient sun light.
MAIN CHARACTERISTICS
Light Transmittance |
3.2mm (1/8”): 90.17%; 4.0mm ( 5/32”): 89.82% |
Solar Transmittance |
3.2mm (1/8”): 84.67%; 4.0mm ( 5/32”): 83.04% |
Certification |
EN12150, EN12600, CCC, SGS, SPF |
Specific weight (kg/m²) |
3.2mm (1/8”): 8 ; 4.0mm ( 5/32”): 10 |
Thickness tolerance |
±0.2mm |
Dimension tolerance |
±1.0mm |
Diagonal difference |
≤0.1-0.2% |
Overall Bow/warp |
﹤0.2% |
Local warp |
≤ 0.3mm / 300mm |
Fragmentation Test |
≥ 40 particles in 25cm² EN12150-1 |
MECHANICAL CHARACTERISTICS
Mechanical strength (N/mm²) |
≥45 Annealed |
≥120 Tempered, EN12150-1 | |
Young modulus (GPa) |
73.1 |
Poisson ratio |
0.2 |
Knoop Hardness (kgf/mm²) |
470 |
Density (kg/m³) |
2500 |
THERMAL CHARACTERISTICS
Hemispherical emissivity (corrected) |
0.84 Between -18℃and 66℃ |
Expansion coefficient (/℃) |
8.6×10﹣6 Between 25℃and 300℃ |
Specific heat |
0.205 Between 0℃ and 100℃ |
Thermal conductivity (W/m/K) |
1 |
Softening point (℃) |
723 |
Annealing point (℃) |
544 |
Strain point (℃) |
504 |
If you want to buy discount and quality clear float solar glass made in China, you can contact Migo Glass which is one of the best manufacturers and suppliers of clear float solar glass in China. We have a professional factory at your service, please feel free to wholesale cheap and customized glass products in stock at a reasonable price with us.